Copolymerization of ethylene with 1‐hexene over metallocene catalyst supported on complex of magnesium chloride with tetrahydrofuran
2004
The study of ethylene/1-hexene copolymerization with the zirconocene catalyst, bis(cyclopentadienyl)zirconium dichloride (Cp 2 ZrCl 2 )/methylaluminoxane (MAO), anchored on a MgCl 2 (THF) 2 support was carried out. The influence of 1-hexene concentration in the feed on catalyst productivity and comonomer reactivity as well as other properties was investigated. Additionally, the effect of support modification by the organoaluminum compounds [(MAO, trimethylaluminum (AlMe 3 ), or diethylaluminum chloride (Et 2 AlCl)] on the behavior of the MgCl 2 (THF) 2 /Cp 2 ZrCl/MAO catalyst in the copolymerization process and on the properties of the copolymers was explored. Immobilization of the Cp 2 ZrC…
Studies on ethylene/1-hexene copolymerization over the zirconocene catalyst supported on MAO-modified MgCl2(THF)2. The effect of copolymerization con…
2002
Badania dotyczą układu katalitycznego MgCl2(THF)2/MAO/Cp2ZrCl2/MAO (MAO — metyloaluminoksan). Stwierdzono, że zarówno aktywność tego układu katalitycznego, jak i właściwości kopolimerów w znacznym stopniu zależą od stosunku molowego Al:Zr (zmienianego w przedziae 1500—7000) i od temperatury kopolimeryzacji (tabele 1 i 2), natomiast wpływ czasu kopolimeryzacji jest mniejszy (tabela 3). Aktywność katalizatora oraz zawartość 1-heksenu wbudowanego do kopolimeru zwiększają się ze wzrostem temperatury i stosunku Al:Zr, a jednocześnie maleje ciężar cząsteczkowy i temperatura topnienia produktów. Ustalono także, że osadzenie katalizatora cyrkonocenowego na stosowanym nośniku powoduje zwiększenie je…
Studies of ethylene/1-hexene copolymerization over zirconocene catalyst supported on MAO-modified MgCl2(THF)2. The effect of copolymerization conditi…
2003
Composition of catalytic system and copolymerization reaction conditions influence on heterogeneity of ethylene/1-hexene copolymers obtained over MgCI2(THF)2/MAO/Cp2ZrCl2/MAO catalyst was studied. One of the DSC techniques, i.e. successive self-nucleation/annealing (SSA) method allowing separation of the polymer into fractions with differing chemical composition in result of alternating crystallization and melting cycles was applied. It was found that the intermolecular heterogeneity exists inside all studied samples irrespective of the reaction conditions (temperature and time) and the catalyst composition (Al/Zr molar ratio). It was also confirmed that catalyst composition has a considera…
Effect of sample preparation on gel permeation chromatography results of determination of molecular weight of polyethylene obtained with using of zir…
2003
Molecular weights of polyethylene (PE) obtained with using of zirconocene catalyst activated with large excess of methylaluminoxane (MAO) were determined by gel permeation chromatography (GPC) method. It was found that repeatability of the measurements is strongly influenced by MAO remained in PE samples as well as time of sample keeping in the apparatus (dissolution + measurement time) at temp. 142 °C. A method of MAO removing from PE samples, before GPC measurement, based on additional washing of the sample with HF in methanol solution has been proposed. This modification leads to better both authenticity and repeatability of the results. Studies on the influence of time of sample keeping…